Anti-Oxidations-Graphitelektroden
Zibo Yinxuan Graphitelektroden Klasse und Referenz Technische Daten
Artikel |
Einheit |
Referenz Technische Daten |
||||||||
Rp |
HP |
SHP |
UHP |
|||||||
≤Ф400mm |
≥Ф450mm |
≤Ф400mm |
≥Ф450mm |
≤Ф400mm |
≥34450mm |
≤Ф400mm |
≥Ф450mm |
|||
Spezifischer Widerstand |
Körper |
ΜΩ · m |
7,0 - 8,5 |
7,5 - 8,8 |
6,0 - 6,8 |
6,2 - 7,0 |
5,5 - 6,5 |
5.8 - 6.5 |
4,5 - 6,0 |
|
Nippel |
|
4.2-5.2 |
3.8-5.0 |
3.5-4.5 |
3,2 - 4,0 |
|||||
Schüttdichte |
Körper |
G / cm³ |
1,54-1,61 |
1,64 - 1,71 |
1,65-1,72 |
1,66-1,73 |
||||
Nippel |
|
1,72-1,77 |
1,74 - 1,78 |
1,75-1,80 |
1,77-1,82 |
|||||
Biegefestigkeit |
Körper |
MPa |
8,5 - 9,5 |
8,0-8,5 |
10,5 - 13,0 |
11,5 - 14,0 |
11,0 - 14,0 |
12.0-15.0 |
||
Nippel |
|
17.0-22.0 |
18,0 - 23,0 |
20.0-25.0 |
21.0-28.0 |
|||||
Elastizitätsmodul |
Körper |
GPa |
8.0-9.3 |
10,0 - 12,0 |
9.0-12.0 |
9.0-14.0 |
||||
Nippel |
|
10.0-14.0 |
10,0 - 16,0 |
10,0-16,0 |
10.0-18.0 |
|||||
CTE (100-600 ℃) |
Körper |
× 10 - 6 / ℃ |
2.1-2.4 |
2,0 - 2,3 |
1.6-1.8 |
1.0-1.4 |
||||
Nippel |
|
2.0-2.3 |
1,8-2,0 |
1.4-1.6 |
0,9-1,3 |
|||||
Asche |
Körper |
% |
≤0.4 |
≤0.3 |
≤0.3 |
≤0.2 |
||||
Nippel |
|
≤0.2 |
≤0.2 |
≤0.2 |
≤0.2 |
|||||
Hauptanwendung |
Angelegt in Lichtbogenöfen oder Tauchbogenöfen zur Herstellung von Stahl, Industriesilizium, Korund, Magnesiumoxid und Phosphor etc. |
Graphitelektroden und Nippel
Graphitelektroden und Nippel
Elektrodengraphit
Graphitelektroden und Nippel
Röhrengraphitelektroden
Graphitnippel
Graphitelektroden und Nippel
Stahlherstellung von Graphitelektroden